The ingot for 5052 aluminum plate roll is melted in the reverberatory furnace and semi continuous casting is carried out. In order to meet the requirements of strict thickness control (5 μ m) in cold rolling, the chemical composition of metal fishing must be controlled within the limits. This is because the change of chemical composition greatly affects the output of the X-ray thickness gauge, that is, the standard value (value) of the metal X-ray absorption calculation is based on the chemical composition of the metal, and the calculated value is fed into the necessary compensation of the cold rolling mill thickness control system.
控制金属的含氢量，消除熔炼和铸造过程中的非金属夹杂物，一直是铸造工程师关注的主要问题。图2所示的在线脱气过滤装置是由铝板制造商开发的。将氩气和氮气混合后，旋转金属中的正常氢气浓度为0.15-0.20ml / 100g Al。铝板制造商的实验室开发了一种奇读气体分析仪。它已成功地用于该威斯尼斯人的在线脱气和过滤系统。气体分析仪是根据类似于Telegas仪器的热物理原理设计的，并使用微处理器进行计算。这些分析仪现在已经可以在铝板制造商之外的地方买到，并且得到了广泛的应用。
Controlling the hydrogen content of metal and eliminating the non-metallic inclusions in smelting and casting process are always the main concerns of foundry engineers. The on-line degassing filter shown in Figure 2 was developed by an aluminum plate manufacturer. After mixing argon and nitrogen, the normal hydrogen concentration in rotating metal is 0.15-0.20ml/100g al. A strange reading gas analyzer has been developed in the laboratory of aluminum plate manufacturer. It has been successfully used in the company's online degassing and filtration system. The gas analyzer is designed according to the thermophysical principle similar to that of the telegas instrument, and is calculated by microprocessor. These analyzers are now available outside the aluminum plate manufacturers and have been widely used.
In order to eliminate or reduce the non-metallic inclusions in the molten metal, the porous ceramic tube filter as shown in Figure 3 is used in the online degasser and filter system. Four porous ceramic filters of different grades (porosity) can be selected as the filter, as shown in Figure 4, class B (y-e, with relatively thick holes (very thin holes). According to the quality requirements of the plate, choose the grade of ceramic pipe. The medium porosity C-type ceramic tube is usually used, but the porosity of D-type ceramic tube is fine, which is used to eliminate the computer disk blank except for the metal inclusion. Practice shows that even if the molten metal is filtered, the metal will occasionally be polluted by the tiny refractory material falling off the filter structure material. In order to ensure the purity of the metal and avoid contamination by inclusions, the proper refractory lining should be selected for the convection tank.
In order to produce high quality anodized plate, the microstructure and metallographic structure of ingot must be fine and uniform. During casting, the molten metal near the ingot surface should be cooled as deep and uniform as possible. Commonly used hot top casting, ceramic fiberboard is attached to the inside of the ingot, as shown in the figure.
以上是澳门威斯尼斯人网址为大家介绍的相关内容，想要了解更多内容，欢迎访问网站：The above is the relevant content introduced by the aluminum plate manufacturer for you. To learn more, please visit the website: http://www.jndclyxgs.com